Edisi : Vol.2, No.1 (2014)
Judul : PENGARUH PERAK PADA FILM FLAVONOID BERBAHAN DASAR GETAH POHON ANGSANA (Pterocarpus indicus Willd) TERHADAP KRISTALINITAS DAN KONDUKTIVITAS LISTRIK
Penulis : NISFI NAHARI SANI HIDAYATI
Markus Diantoro
Abdulloh Fuad
Abstrak :

ABSTRAK


 


 


Hidayati Nisfi Nahari Sani. 2014. Pengaruh Perak Pada Film Flavonoid Berbahan Dasar Getah Pohon Angsana (Pterocarpus indicus Willd) Terhadap Kristalinitas dan Konduktivitas Listrik. Skripsi Jurusan Fisika Fakultas MIPA Universitas Negeri Malang. Pembimbing: (I) Dr. Markus Diantoro M.Si. (II) Drs. Abdulloh Fuad M.Si.


 


Kata Kunci: getah pohon Angsana (Pterocarpus indicus Willd) film perak spin coating kristalinitas konduktivitas listrik.


 


Getah merupakan cairan yang keluar dari bagian tumbuhan seperti pada daun atau batang. Salah satu pohon di Indonesia yang memiliki getah banyak adalah pohon angsana (Pterocarpus indicus Willd). Getah pohon Angsana ini mengandung polimer alam. Senyawa kimia yang terkandung pada tumbuhan angsana yaitu flavanoid yang memiliki kerangka karbon C6-C3-C6. Untuk memperoleh conducting polymer yang baik maka perlu memodifikasi sifat getah. Hal ini dapat dilakukan menambahkan Ag  pada getah pohon Angsana. Perak memiliki sifat listrik yang terbaik dibandingkan dengan logam lain karena nilai konduktivitas listrik perak paling tinggi. Penelitian ini bertujuan untuk mengetahui pengaruh perak terhadap kristalinitas dan konduktivitas listrik film getah Angsana-Ag.


Metode spin coating digunakan untuk menumbuhkan film diatas substrat nikel. Gugus fungsi yang terdapat pada getah Angsna dikarakterisasi dengan menggunakan FTIR. Kristalinitas film getah Angsana-Ag dikarakterisasi menggunakan XRD. Fotografi permukaan film getah Angsana-Ag dapat dilihat dengan uji SEM. Untuk mengetahui unsur yang terkandung dalam film Flavonoid getah Angsana maka dilakukan pengujian EDAX. Konduktivitas listrik diuji dengan menggunakan metode four point probe.


Hasil analisis FTIR yang diperoleh menghasilkan gugus fungsi C-H aromatik C-O aromatik C-O alkohol C-H C=C aromatik C-H alifatik dan -OH dapat dikatakan senyawa flavonoid ini termasuk dalam jenis rutin (Hussain 2009). Penambahan Ag mempengaruhi kristalinitas film getah-Ag. Hasil yang diperoleh dari karakterisasi XRD menunjukkan adanya peningkatan kristalinitas untuk variasi doping 0.1 M 0.2 M 0.3 M 0.4 M dan 0.5 M yaitu 0.66 % 0.95 % 1.94 % 3.37 % dan 4.11%. Fotografi SEM menunjukkan adanya butiran-butiran yang merupakan unsur Ag. Hasil pengujian EDAX diperoleh persentase At unsur Ag untuk 0.1 M dan 0.2 M tidak ada karena massa doping terlalu sedikit sedangkan untuk variasi doping 0.3 M 0.4 M dan 0.5 M terjadi peningkatan 3.60 % 3.66% dan 4.20 %. Sifat kelistrikan yaitu konduktivitas listrik akan naik seiring dengan penambahan Ag. Nilai konduktivitas listriknya adalah 3.22 S/cm 95.73 S/cm 391.56 S/cm 428.05 S/cm dan 542.85 S/cm.


 


 


 


 


ABSTRACT


 


 


Hidayati Nisfi Nahari Sani. 2014. The Influence of Silver on Crystallinity and Electric Conductivity of Flavonoid Angsana’s Latex (Pterocarpus indicus Willd) Film. Thesis Physics Department Faculty of Mathematics and Science State University of Malang. Advisors: (I) Dr. Markus Diantoro M.Si. (II) Drs. Abdulloh Fuad M.Si.


 


Key words: latex Angsana tree (Pterocarpus indicus Willd) silver doping (Ag) spin coating method crystallinity electric conductivity FTIR XRD SEM EDAX.


 


Latex is kind of liquid which is found in the part of a plant such as in the leave or stem. One of kind of tree in Indonesia which has a great amount of latex is Angsana tree (Pterocarpus indicus Willd). Angsana’s latex contains natural polymer. In addititon Angsana tree contains chemical compound so-called flavonoid which has C6-C3-C6 carbon design. Therefore to gain good conducting polymer the latex nature should be modified. It can be done with adding silver (Ag) on Angsana’s latex. As we know silver has the best electric nature than other metals because the conductivity value of silver electric is high. Thus this research has aim to know the influence of Ag adding on crystallinity and electric conductivity of Flavonoid Angsana’s latex -Ag film.


Spin coating method is used to grow film upon nickel substrat. Functional group of Angsana’s latex is characterized using FTIR. Moreover crystallinity of Ag-latex film is characterized using XRD. The photography of Ag-latex film surface can be seen using SEM test. In order to know what compound is contained by Angsana’s latex film it has to do EDAX test. Meanwhile the electric conductivity is tested using four point probe method.


The result of analysis of FTIR produces C-H aromatic functional group C-O alcohol C-H C=C aromatic C-H alifatic and –OH. Hence it can be conclued that flavonoid compound belongs to kind of rutin (Hussain 2009). The addition of Ag also influence crystallinity of Flavonoid Angsana’s latex-Ag film. The result of XRD characterization shows that there is crystalinity increase for the variety of doping 0.1 M 0.2 M 0.3 M 0.4 M and 0.5 M in the amount of 0.66% 0.95% 1.94% 3.37% and 4.11%. SEM photography shows that there are some grains of Ag compound. EDAX’s test result shows that there is no Ag compound on At percentage for 0.1 M and 0.2 M because the doping mass is only few; on the other hand for the variety of doping 0.3 M 0.4 M and 0.5 M shows that there is percentage increase in the amount of 3.60% 3.66% and 4.20%. The nature of electric precisely electric conductivity will increase as well as the addition of Ag. Therefore the electric conductivity values are 3.22 S/cm 95.73 S/cm 391.56 S/cm 428.05 S/cm and 542.85 S/cm.

Kata Kunci : getah; pohon Angsana (Pterocarpus indicus Willd);film;perak;spin coating;kristalinitas;konduktivitas listrik